Тесты на реальность, как по составу так и по твёрдости стали на клинке!
Batch 2 Test
LTK Rezult (20CV)(Yes) V 4.42 Cr 19.47 Fe 73.78 Mo 1.06 W .437 60.1 HRC 20CV
TwoSun Vandal (M390)(Yes) V 4.69 Cr 19.74 Fe 73.83 Mo 1.03 W .454 59.2 HRC M390
Microtech MSI (M390)(Yes) V 4.51 Cr 19.76 Fe 73.15 Ni .307 Mo 1.08 W .377 58.7 HRC M390
XTOUC SX603 button lock (14C)(Yes) Cr 14.13 Mn .655 Fe 84.71 Ni .217 Mo .126 59.8 HRC Aeb-L
14C28N composition Carbon C 0.62% Chromium Cr 14.00% Manganese Mn 0.60% Nitrogen N 0.11% Silicon Si 0.30% Phosphorus P 0.02% Sulfur S 0.01 ** 14C vs AEB-L These steels are nearly identical. If anyone can tell the difference between these two steels based on performance, it has less to do with the difference in chemistry and more to do with the different HT protocols being implemented, which would be true if you compared 13C26/AEB-L against itself with two different HT protocols - one to maximize hardness, the other to maximize corrosion resistance. 14C28N swaps out some carbon for nitrogen and adds more chromium to get a tiny bit more 'stainless'.
Kizer Clairvoyant (S35VN)(Yes) V. 3.47 Cr 14.26 Fe 78.84 Nb .595 Mo 2.18 59.6 HRC S35VN
Vosteed Thunderbird (S35VN)(Yes) V 3.64 Cr 14.32 Fe 78.57 Nb .616 Mo 2.02 61.0 HRC S35vn
Todd Begg Bodega (D2)(Yes) V .733 Cr 11.81 Fe 83.86 Mo .892 62.1 HRC D2
CJRB Pyrite (AR-RPM9)(Yes) V .106 Cr 17.46 Mn .593 Fe 80.53 Mo 1.14 59.9 HRC 440c or similar (I'm calling it AR-RPM9)
AR-RPM9 (Published Composition) C 0.90 Cr 18.00 Mo 1.0 V .10 Co .30 Ni 0.00-0.40 Mn 0.45 Si 0.20-0.80
Civivi Sinisys (14c28n)(Yes) Cr 13.71 Mn .754 Fe 85.24 Mo .128 60.0 HRC Aeb-L (I'm calling it 14C28N)
Kizer Sheepdog (154CM)(Yes) V .285 Cr 13.42 Fe 81.29 Mo 4.15 59.6 HRC 154cm
Fat Dragon Divinity Tree (M390)(Yes) V 4.38 Cr 18.93 Fe 74.17 Ni .274 Mo 1.08 W .598 58.2 HRC M390
Remette Peacock (9CR18MOV)(Yes) V .084 Cr 16.68 Fe 82.00 Mo .455 61.7HRC 9cr18mov
Sitivien ST996 (M390)(Yes) V 4.01 Cr 19.72 Fe 74.34 Ni .269 Mo 1.03 W .452 58.2 HRC M390
Protech Rockeye (S35VN)(Yes) V 3.24 Cr 14.04 Fe 79.32 Nb .596 Mo 2.06 59.9 HRC S35vn
HUAAO (M390)(Not) V .171 Cr 13.93 Fe 85.04 Mo .565 61.3 HRC Aeb-L (but maybe 14C28N)
SMKE Arius (clone) knife (M390)(Yes) V 4.80 Cr 20.03 Fe 72.63 Mo 1.04 W .420 60.2 HRC M390
Olitans (M390)(No) V .088 Cr 17.01 Fe 81.29 Mo .649 58.4 HRC 440C or similar (maybe 9cr18 ?)
Kunwu Pulsar (Elmax)(Yes) V 3.47 Cr 18.58 Fe 76.54 Ni .353 Mo .922 60.3 HRC Elmax
Химия похожа, но китайцы калят m390 на меньшую твердость чем 9cr18,это конечно тупость, вот НОКС например это учла и майор свой новый закалила на 61-63. Ну и вообще не понятная AR-RPM9,заявлялась как первый порошок от китайцев, а по факту не лучше обычных среднебюджетных сталей по отзывам.
судя по результатам этого же дятьки, не только китайцы- в этом же видео он вспоминает только одну парамилю, за все тесты м390, где закалили на 62 что ли...
С заявленной твёрдостью у всех нормально: Sitivien ST996- 60-62HRC, по факту-58.2; Fat Dragon DIVINITY TREE- обещают скромнее- 59-60HRC, на деле, те же 58.2 (термичат там же?)
по началу нашёл на али.. . Потом увидел на авито, под названием "нож Широгорова", нафига не понятно, по мне так самодостаточное изделие. Доберусь до Нерезиновой, потрогаю в живую